Impacters of various shapes and masses were dropped from various heights onto 36 mm (1.4 in.) thick graphite/epoxy cylinders, which represented filament wound cases (FWC) for the booster motors of the Space Shuttle. Insert solid propellant was cast into some of the cylinders. The cylinders were impacted numerous times around the circumference and then cut into 51 mm (2.0 in.) wide tension specimens, each containing an impact site. Four indenters were used: a sharp corner, two hemispheres, and a bolt-like rod. The diameters of the hemispheres were 12.7 mm mm (0.5 in.) and 25.4 mm (1.0 in.), and the diameter of the rod was 6.3 mm (0.25 in.). Impacts with the rod were simulated by pressing the rod against the face of specimens. For the hemispheres, the damage initiated beneath the surface at a critical contact pressure and was not visible on the surface until an even larger pressure was exceeded. The damage consisted of matrix cracking and broken fiber. The rod an corner made visible surface damage in all tests. For the hemispheres, the tension strength was reduced considerably before the damage was visible on the surface, 30 percent for the 25.4 mm (1.0 in.) diameter hemisphere and 10 percent for the 12.7 mm (0.5 in.) diameter hemisphere. Analytical methods were used to predict the damage and residual tension strength. A factor of safety to account for nonvisible damage was determined. Poe, C. C., Jr. Langley Research Center RTOP 505-63-01-05...